Semiconductor apparatus

ABSTRACT

A method for fabricating a semiconductor apparatus including providing a first silicon substrate having a first contact, wherein providing the first silicon substrate comprises forming a silicide layer between the first silicon substrate and a first metal layer. The method further includes providing a second silicon substrate having a second contact comprising a second metal layer and placing the first contact in contact with the second contact. The method further includes heating the first and second metal layers to form a metallic alloy, whereby the metallic alloy bonds the first contact to the second contact.

CROSS-REFERENCE TO RELATED APPLICATION

The present application is a divisional of U.S. application Ser. No. 13/048,127, filed Mar. 15, 2011, which is incorporated herein in its entirety.

FIELD OF THE INVENTION

The invention relates to integrated circuit fabrication, and more particularly to a semiconductor apparatus with a metallic alloy.

BACKGROUND

Micro-electro-mechanical system (MEMS) technology is the integration of very small mechanical devices installed inside a silicon substrate such as sensors, valves, gears, reflecting mirrors, and drivers on a computer. Thus, MEMS devices are often called intelligent machines. To protect against external interference during operation, it may be desirable to bond with a cap substrate to hermetically seal the MEMS devices to form a semiconductor apparatus. Furthermore, in many applications, it is also desirable for the bonded substrates to include integrated circuit (IC) devices.

However, there are challenges to implementing such features and processes in MEMS or IC device fabrication. For example, in a “substrate bonding” process, it is difficult to achieve a low-contact-resistance bond between bonded substrates because high-contact-resistance materials are generated in the interface between the bonded substrates, thereby increasing the likelihood of semiconductor apparatus instability and/or semiconductor apparatus failure.

Accordingly, what is needed is a method to form a low-contact-resistance bond between bonded substrates.

SUMMARY

In one embodiment, a semiconductor apparatus comprises a first silicon substrate having a first contact comprising a silicide layer between the substrate and a first metal layer; a second silicon substrate having a second contact comprising a second metal layer; and a metallic alloy between the first metal layer of the first contact and the second metal layer of the second contact.

In another embodiment, a method for fabricating a semiconductor apparatus comprises providing a first silicon substrate having a first contact comprising a silicide layer between the substrate and a first metal layer; providing a second silicon substrate having a second contact comprising a second metal layer; placing the first contact in contact with the second contact; and heating the first and second metal layers to form a metallic alloy, whereby the metallic alloy bonds the first contact to the second contact.

A detailed description is given in the following embodiments with reference to the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 is a flowchart illustrating a method for fabricating a semiconductor apparatus comprising a metallic alloy according to various aspects of the present disclosure;

FIGS. 2A-2F show schematic cross-sectional views of a metallic alloy of a semiconductor apparatus at various stages of fabrication according to various aspects of the present disclosure; and

FIG. 3 is a cross-sectional view of a semiconductor apparatus having a metallic alloy fabricated using the steps shown in FIG. 2A-2F.

DESCRIPTION

It is understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. Various features may be arbitrarily drawn in different scales for simplicity and clarity. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Referring to FIG. 1, illustrated is a flowchart of a method 100 for fabricating a semiconductor apparatus comprising a metallic alloy according to various aspects of the present disclosure. The method 100 begins with step 102 in which a first silicon substrate having a first contact comprising a silicide layer between the substrate and a first metal layer is provided. The method 100 continues with step 104 in which a second silicon substrate having a second contact comprising a second metal layer is provided. The method 100 continues with step 106 in which the first contact is placed in contact with the second contact. The method 100 continues with step 108 in which the first and second metal layers are heated to form a metallic alloy, whereby the metallic alloy bonds the first contact to the second contact. The discussion that follows illustrates an embodiment of a method in accordance with FIG. 1.

FIGS. 2A-2F show schematic cross-sectional views of a metallic alloy 220 of a semiconductor apparatus 200 at various stages of fabrication according to various aspects of the present disclosure. It is noted that the method of FIG. 1 does not produce a completed semiconductor apparatus 200. Accordingly, it is understood that additional processes may be provided before, during, and after the method 100 of FIG. 1, and that some other processes may only be briefly described herein. Also, FIGS. 2A through 2F are simplified for a better understanding of the inventive concepts of the present disclosure. For example, although the figures illustrate the metallic alloy 220 of a semiconductor apparatus 200, it is understood the semiconductor apparatus 200 may be part of an integrated circuit that further comprises a number of other components such as under-fill, lead-frame, etc.

Referring to FIGS. 2A-2D, a first silicon substrate 202 is provided. The step of providing the first silicon substrate 202 may further comprise partially fabricating a first contact 210 comprising a silicide layer 208 between the substrate 202 and a first metal layer 206. The first silicon substrate 202 may comprise a pure silicon substrate. In another embodiment, the first silicon substrate 202 may be a semiconductor on insulator, such as silicon on insulator (SOI) or silicon on sapphire. In other embodiments, the substrate 202 may comprise a doped epitaxial (epi) layer, a gradient semiconductor layer, and/or may further include a semiconductor layer overlying another semiconductor layer of a different type, such as a silicon layer on a silicon germanium layer.

In one embodiment, the first silicon substrate 202 may further comprise a plurality of microelectromechanical system (MEMS) devices (not shown). The MEMS devices are the integration of very small mechanical devices installed inside the first silicon substrate 202 such as sensors, valves, gears, reflecting mirrors, and drivers on a computer. Therefore, the MEMS devices can be used for a variety of devices including oscillators, channels, pumps, accelerometers, and filters. The MEMS devices may be manufactured using surface micromechanics, deposition, or etching technologies.

In another embodiment, the first silicon substrate 202 may further comprise a plurality of isolation features (not shown), such as shallow trench isolation (STI) features or local oxidation of silicon (LOCOS) features. The isolation features may define and isolate various microelectronic elements (not shown).

Examples of the various microelectronic elements that may be formed in the first silicon substrate 202 comprise transistors (e.g., p-channel/n-channel metal oxide semiconductor field effect transistors (pMOSFETs/nMOSFETs), bipolar junction transistors (BJTs), high voltage transistors, high frequency transistors, etc.); diodes; resistors; capacitors; inductors; fuses; and other suitable elements. Various processes are performed to form the various microelectronic elements including deposition, photolithography, implantation, etching, annealing, and other suitable processes. The microelectronic elements are interconnected to form an integrated circuit (IC) device, such as a logic device, memory device (e.g., static random access memory or SRAM), radio frequency (RF) device, input/output (I/O) device, system-on-chip (SoC) device, combinations thereof, and other suitable types of devices.

The substrate 202 further comprises inter-layer dielectric (ILD) layers, inter-metal dielectric (IMD) layers and a metallization structure overlying the IC device. The IMD layers in the metallization structure include low-k dielectric materials, un-doped silicate glass (USG), fluorine-doped silicate glass (FSG), carbon-doped silicate glass, silicon nitride, silicon oxynitride, or other materials. The dielectric constants (k value) of the low-k dielectric materials may be less than about 3.9, or less than about 2.3. Metal lines in the metallization structure may be formed of aluminum, aluminum alloy, copper, copper alloys, or other conductive materials. One skilled in the art will realize the formation details of the metallization structure.

Still referring to FIG. 2A, the first silicon substrate 202 further comprises a raised portion 202 a for electrically connecting the MEMS device or IC device to an external contact, and lowered portions 202 b to accommodate proof mass of the MEMS device. Various processes are performed to form the raised portion 202 a including photolithography, etching and other suitable processes. While only one raised portion 202 a is illustrated as being formed in the first silicon substrate 202, it is understood that any number of raised portions 202 a may be formed in the first silicon substrate 202.

Referring to FIG. 2B, after the raised portion 202 a formation process, a first metal layer 206 is then deposited over and extending out of the lowered portions 202 b and onto the raised portion 202 a. In one embodiment, the first metal layer 206 comprises a material selected from a group of Ti, Co, Ni, W, and Pt. The first metal layer 206 may be formed by chemical vapor deposition (CVD), physical vapor deposition (PVD) or other suitable technique. In the present embodiment, the first metal layer 206 has a thickness t₁ ranging from 300 to 1000 angstroms.

Referring to FIG. 2C, following deposition of the first metal layer 206 over and extending out of the lowered portions 202 b and onto the raised portion 202 a, an anneal process may be performed to the intermediate semiconductor apparatus 200 in FIG. 2B to form a silicide layer 208 between the first silicon substrate 202 and the first metal layer 206. The anneal process can be performed, for example, in a furnace, a rapid thermal anneal (RTA) system or other thermal system that is adapted to provide a thermal treatment for a reaction between the first silicon substrate 202 and the first metal layer 206 to form the silicide layer 208. Therefore, the silicide layer 208 is on the first metal layer 206. In some embodiments, the anneal process may be performed at a temperature of about 650° C. to 900° C. for about 30 seconds in a RTA system.

In one embodiment, the silicide layer 208 comprises a material selected from a group of Ti, Co, Ni, W, and Pt. In the present embodiment, the silicide layer 208 may comprise a material selected from titanium silicide, cobalt silicide, and nickel silicide. The silicide layer 208 can provide a low-resistance path between the substrate 202 and the first metal layer 206 for good overall electrical conductivity. In one embodiment, the silicide layer 208 has a thickness t₂ ranging from 300 to 600 angstroms. The resulted thickness of the first metal layer 206 is thinned to a thickness t₃ due to consumption for formation of the silicide layer 208. In the present embodiment, a thickness ratio (t₃/t₂) of the first metal layer 206 to the silicide layer 208 is from about 1 to 2.

Then, a layer of photoresist (not shown) is formed over the first metal layer 206 by a suitable process, such as spin-on coating, and patterned to form a patterned photoresist feature by a proper lithography patterning method. A width of the patterned photoresist feature is in the range of about 30 to 80 μm. The patterned photoresist feature can then be transferred using a dry etching process to the underlying layers (i.e., the first metal layer 206 and the silicide layer 208) to form a first contact 210 (shown in FIG. 2D). The first contact 210 is used in the bonding process to electrically connect the MEMS device or IC device in the respective silicon substrate to external features, such as a second contact 310 of the second silicon substrate 302 (shown in FIG. 2E). A first width W₁ of the first contact 210 is in the range of about 30 to 80 μm. The photoresist layer may be stripped thereafter.

The first silicon substrate 202 is then bonded onto a second silicon substrate 302 to form the semiconductor apparatus 200. The structure of FIG. 2E shows the first silicon substrate 202 is flipped upside down and engaged with the second silicon substrate 302 at the bottom. The second silicon substrate 302 may comprise a pure silicon substrate. In another embodiment, the second silicon substrate 302 may be a semiconductor on insulator, such as silicon on insulator (SOI) or silicon on sapphire. In other embodiments, the second silicon substrate 302 may comprise a doped epi layer, a gradient semiconductor layer, and/or may further include a semiconductor layer overlying another semiconductor layer of a different type, such as a silicon layer on a silicon germanium layer.

In one embodiment, the second silicon substrate 302 may further comprise a plurality of microelectromechanical system (MEMS) devices (not shown). The MEMS devices are the integration of very small mechanical devices installed inside the second silicon substrate 302 such as sensors, valves, gears, reflecting mirrors, and drivers on a computer. Therefore, the MEMS devices can be used for a variety of devices including oscillators, channels, pumps, accelerometers, and filters. The MEMS devices may be manufactured using surface micromechanics, deposition, or etching technologies.

In another embodiment, the second silicon substrate 302 may further comprise a plurality of isolation features (not shown), such as shallow trench isolation (STI) features or local oxidation of silicon (LOCOS) features. The isolation features may define and isolate various microelectronic elements (not shown).

Examples of the various microelectronic elements that may be formed in the second silicon substrate 302 include transistors (e.g., p-channel/n-channel metal oxide semiconductor field effect transistors (pMOSFETs/nMOSFETs), bipolar junction transistors (BJTs), high voltage transistors, high frequency transistors, etc.); diodes; resistors; capacitors; inductors; fuses; and other suitable elements. Various processes are performed to form the various microelectronic elements including deposition, photolithography, implantation, etching, annealing, and other suitable processes. The microelectronic elements are interconnected to form an integrated circuit (IC) device, such as a logic device, memory device (e.g., static random access memory or SRAM), radio frequency (RF) device, input/output (I/O) device, system-on-chip (SoC) device, combinations thereof, and other suitable types of devices.

The second silicon substrate 302 further comprises inter-layer dielectric (ILD) layers, inter-metal dielectric (IMD) layers and a metallization structure overlying the integrated circuit device (not shown). The IMD layers in the metallization structure include low-k dielectric materials, un-doped silicate glass (USG), fluorine-doped silicate glass (FSG), carbon-doped silicate glass, silicon nitride, silicon oxynitride, or other commonly used materials. The dielectric constants (k value) of the low-k dielectric materials may be less than about 3.9, or less than about 2.3. Metal lines in the metallization structure may be formed of aluminum, aluminum alloy, copper, copper alloys, or other conductive materials. One skilled in the art will realize the formation details of the metallization structure.

The second silicon substrate 302 further comprises a second contact 310. The second contact 310 is a top metallization layer formed in a top-level IMD layer, which is a portion of conductive routes and has an exposed surface treated by a planarization process, such as chemical mechanical polishing (CMP), if necessary. The second contact 310 is used in the bonding process to electrically connect the MEMS device or IC device in the respective silicon substrate to external features, such as the first contact 210 of the first silicon substrate 202. In other words, the first contact 210 is placed in contact with the second contact 310 (shown in FIG. 2E). In one embodiment, a second width W₂ of the second contact 310 is greater than the first width W₁ of the first contact 210. In another embodiment, the second width W₂ of the second contact 310 is less than the first width W₁ of the first contact 210. In the present embodiment, a width ratio (W₁/W₂) of the first contact 210 to the second contact 310 is from about 0.12 to 1.2.

The second contact 310 may comprise a second metal layer 306. Suitable materials for the second metal layer 306 may comprise, but are not limited to, for example Al, Al alloy, or other conductive materials. The second metal layer 306 may be formed by chemical vapor deposition (CVD), physical vapor deposition (PVD) or other suitable technique. In the present embodiment, the second metal layer 306 has a thickness t₄ ranging from 7500 to 8500 angstroms. In one embodiment, a thickness ratio (t₄/t₂) of the second metal layer 306 to the silicide layer 208 is from about 12 to 25.

Before placing the first contact 210 in contact with the second contact 310, native oxides (not shown) may form on an exposed top surface of the first metal layer 206, as well as a top surface of the second metal layer 306 due to exposure to air. The native oxides need to be cleaned (i.e., removed) because the first and second metal layers 206, 306 will not alloy with each other with the native oxides between the first and second metal layers 206, 306.

In current embodiments of the disclosure, a pre-clean process to remove the native oxides is performed in a pre-clean chamber with a reducing gas, such as hydrogen or NH₃, and an inert gas, such as argon, helium or nitrogen. The ratio of the reducing gas to the inert gas depends upon such factors as the particular reaction chamber being used and the particular gasses being used.

In one embodiment, the reducing gas is hydrogen and the inert gas is helium. The hydrogen reactive pre-clean process advantageously removes the native oxide by reducing the native oxide without physical bombardment. Thus, the native oxide can be removed without damaging the exposed top surface of the first metal layer 206, as well as the top surface of the second metal layer 306. This facilitates attempts to form and maintain precise separation distances between the two silicon substrates 202, 302 because the first metal layer 206 and the second metal layer 306 both remain relatively smooth.

The process steps up to this point have provided the silicon substrates 202, 302 having fresh and smooth surfaces to make it easier for alloying the first metal layer 206 and the second metal layer 306 with each other. This can reduce defect generation in the interface between the bonded silicon substrates 202, 302 and upgrade semiconductor apparatus performance.

Referring to FIG. 2F, after placing the first contact 210 in contact with the second contact 310, the first and second metal layers 206, 306 are heated to form a metallic alloy 220, whereby the metallic alloy 220 bonds the first contact 210 to the second contact 310. Although other pressures are also possible, the two silicon substrates 202, 302 are pressed together under a compressive force of about 45 to 55 kN to form a weak bond between the first contact 210 and the second contact 310.

The pressed silicon substrates 202, 302 are then placed in an annealing chamber. A bonding process is then performed on the structure of the semiconductor apparatus 200 by varying the temperature within the annealing chamber in order to form the metallic alloy 220 by alloying the first and second metal layers 206, 306, which couples the two silicon substrates 202, 302. In this regard, the temperature of the annealing chamber is increased to about 480° C. within about 60 seconds once the pressed silicon substrates 202, 302 are placed in the annealing chamber. Although not necessary for implementing the invention, the temperature may change linearly (i.e., “ramp” the temperature) when the temperature of the annealing chamber is being varied.

In the present embodiment, the step of heating is performed under a compressive force of about 45 to 55 kN and at a temperature of about 450° to 500° C. for about 40 minutes. It should be noted that other annealing temperatures and durations are possible for forming a sufficient bond between the silicon substrates 202, 302. A bond is “sufficient” for the purposes of the present disclosure when it is capable of maintaining an alignment of the first silicon substrates 202 with respect to the second silicon substrates 302 during normal operation of the semiconductor apparatus 200.

After maintaining the annealing temperature for the prescribed time, the temperature of the annealing chamber is decreased below about 100° C. in about 6 minutes. One skilled in the art should realize that other temperatures and times are possible for the bonding process.

At this point, the metallic alloy 220 may bond the first and second metal layers 206, 306, and be sufficient to keep first silicon substrates 202 attached and aligned to the second silicon substrates 302. In other words, the metallic alloy 220 provides the semiconductor apparatus 200 with mechanical support and low-resistance connection, and the other conductive material such as the silicide layer 208 provides an electrical connection between the MEMS device of the first silicon substrate 202 and the IC device of the second silicon substrate 302. In one embodiment, one of the first or second silicon substrates 202, 302 comprises a micro-electromechanical system (MEMS) device and the other substrate comprises an integrated circuit (IC) device. In another embodiment, the first silicon substrate 202 comprises a micro-electromechanical system (MEMS) device and the second silicon substrate 302 comprises an integrated circuit (IC) device. Accordingly, Applicant's method of fabricating a semiconductor apparatus 200 may fabricate a low-resistance metallic alloy for bonding the silicon substrates 202, 302 and upgrade semiconductor apparatus performance.

In the present embodiment, the metallic alloy 220 comprises an alloy of the first and second metal layers 206, 306. The metallic alloy 220 may comprise a metallic compound. In the present embodiment, the metallic compound comprises Al. In one embodiment, the metallic compound may comprise Ti_(x)Al_(y) such as TiAl or TiAl₃, in which the first metal layer 206 comprises Ti and the second metal layer 306 comprises Al. In another embodiment, the metallic compound may comprise Ni_(x)Al_(y) such as NiAl₃, Ni₂Al₃, NiAl, or Ni₃Al, in which the first metal layer 206 comprises Ni and the second metal layer 306 comprises Al. In still another embodiment, the metallic compound may comprise Co_(x)Al_(y) such as Co₂Al₅ or Co₄Al₁₃, in which the first metal layer 206 comprises Co and the second metal layer 306 comprises Al. In still another embodiment, the metallic compound may comprise Al_(x)W_(y) such as Al₁₂W, Al₅W, or Al₄W, in which the first metal layer 206 comprises W and the second metal layer 306 comprises Al. In still another embodiment, the metallic compound may comprise Pt_(x)Al_(y) such as Pt₂Al₃, in which the first metal layer 206 comprises Pt and the second metal layer 306 comprises Al. In the present embodiment, the metallic alloy 220 has a thickness t₅ ranging from 500 to 1500 angstroms. In one embodiment, a thickness ratio (t₅/t₂) of the metallic alloy 220 to the silicide layer 208 is from about 0.8 to 5.

FIG. 3 is a cross-sectional view of a semiconductor apparatus 300 having a metallic alloy 220 fabricated using the steps shown in FIG. 2A-2F. A supporting mechanism (not shown) elastically supports mass proof of MEMS device 320, such as a mirror on the first silicon substrate 202, in which the mirror floats from the first silicon substrate 202, so that the mirror can be inclined in an arbitrary direction. On the other hand, mass proof of MEMS device 320, such as a rotor, may be floating above the second silicon substrate 302 and controlled by a driving structure (not shown). It is understood that the semiconductor apparatus 300 may undergo further IC processing to form various features such as under-fill, lead-frame, etc.

One aspect of this description relates to a method for fabricating a semiconductor apparatus. The method includes providing a first silicon substrate having a first contact, wherein providing the first silicon substrate comprises forming a silicide layer between the first silicon substrate and a first metal layer. The method further includes providing a second silicon substrate having a second contact comprising a second metal layer and placing the first contact in contact with the second contact. The method further includes heating the first and second metal layers to form a metallic alloy, whereby the metallic alloy bonds the first contact to the second contact.

Another aspect of this description relates to a method of fabricating a semiconductor device. The method includes depositing a first metal layer over a first substrate and annealing the first substrate to form a silicide layer between the first metal layer and the first substrate and defining a first contact comprising on the first metal layer and the silicide layer. The method further includes depositing a second metal layer over a second substrate and defining a second contact comprising the second metal layer. The method further includes pressing the first contact to the second contact and heating the first contact and second contact to form a metallic alloy between the first contact and the second contact.

Still another aspect of this description relates to a method of fabricating a semiconductor device. The method includes defining a plurality of first contacts. Each first contact of the plurality of first contacts includes at least one raised portion on a surface of a first substrate; a silicide layer over the at least one raised portion; and a first metal layer over the at least one raised portion. The method further includes defining a plurality of second contacts, wherein each second contact of the plurality of second contacts comprises a second metal layer over a second substrate. The method further includes pressing each first contact of the plurality of first contacts to a respective second contact of the plurality of second contacts. The method further includes heating the plurality of first contacts and the plurality of second contacts to form a metallic alloy between each of the first contacts of the plurality of first contacts pressed to the respective second contacts of the plurality of second contacts.

While the disclosure has been described by way of example and in terms of the above embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements. 

What is claimed is:
 1. A method for fabricating a semiconductor apparatus comprising: providing a first silicon substrate having a first raised portion and a lower portion and a first contact, wherein providing the first silicon substrate comprises forming a silicide layer between the first silicon substrate and a first metal layer, and the first metal layer is on the first raised portion and a region of the lower portion surrounding the first raised portion such that a first portion of the first metal layer on the first raised portion is separate from a second portion of the first metal layer on a second raised portion, the first metal layer comprising Ti, Co, Ni, W, or Pt; providing a second silicon substrate having a second contact comprising a second metal layer, wherein the second metal layer comprises Al or Cu; placing the first contact in contact with the second contact; and heating the first and second metal layers to form a metallic alloy, whereby the metallic alloy bonds the first contact to the second contact.
 2. The method of claim 1, wherein the heating is performed at a temperature of about 450° to 500° C.
 3. The method of claim 1, wherein the heating is performed under a compressive force of about 45 to 55 kN.
 4. The method of claim 1, wherein forming the silicide layer comprises reacting the first silicon substrate and first metal layer.
 5. The method of claim 1, wherein providing the first silicon substrate comprises defining a width of the first contact, wherein the width of the first contact ranges from 30 micrometers (μm) to 80 μm.
 6. The method of claim 5, wherein providing the second silicon substrate comprises defining a width of the second contact, wherein a ratio of the width of the first contact to a width of the second contact ranges from 0.12 to 1.2.
 7. The method of claim 1, further comprising cleaning a surface of the second contact by exposing the surface to a reduction gas prior to placing the first contact in contact with the second contact.
 8. The method of claim 1, wherein forming the metallic alloy comprises forming the metallic alloy having a thickness ranging from 500 Angstroms (Å) to 1500 Å.
 9. A method of fabricating a semiconductor device, the method comprising: depositing a first metal layer onto a first raised portion and a second raised portion of a first substrate and a region of a lower portion of the first substrate surrounding each of the first raised portion and the second raised portion such that the first metal layer is discontinuous between the first raised portion and the second raised portion; annealing the first substrate to form a silicide layer between the first metal layer and the first substrate; defining a first contact comprising the first metal layer and the silicide layer; depositing a second metal layer over a second substrate; defining a second contact comprising the second metal layer; pressing the first contact to the second contact; and heating the first contact and second contact to form a metallic alloy between the first contact and the second contact, wherein the metallic alloy is an alloy of the first metal layer and the second metal layer.
 10. The method of claim 9, wherein the heating is performed by annealing the first contact and the second contact at a plurality of temperatures.
 11. The method of claim 9, further comprising cleaning a surface of the second contact by exposing the surface to a reduction gas prior to pressing the first contact to the second contact.
 12. The method of claim 11, wherein exposing the surface to reduction gases comprises exposing the surface to at least one of hydrogen or ammonia.
 13. The method of claim 9, wherein forming the metallic alloy comprises forming an alloy comprising aluminum.
 14. The method of claim 9, wherein heating the first and second contact comprises performing an annealing process at a temperature ranging from about 450° C. to about 500° C.
 15. The method of claim 9, wherein pressing the first contact to the second contact comprises exerting a force ranging from about 45 kiloNewtons (kN) to about 55 kN.
 16. The method of claim 9, wherein annealing the first substrate to form the silicide layer comprises annealing the first substrate at a temperature ranging from about 650° C. to about 900° C.
 17. A method of fabricating a semiconductor device, the method comprising: defining a plurality of first contacts, wherein the plurality of first contacts comprises: a first substrate having a lower portion and a first raised portion and a second raised portion of at least one raised portion a surface of the first substrate; a silicide layer over the at least one raised portion; and a first metal layer over the at least one raised portion, wherein a first segment of the first metal layer is over the first raised portion and a second segment of the first metal layer is over the second raised portion and over a region of the lower portion surrounding the first and second raised portions, and wherein the metal layer is discontinuous between each of the at least one raised portion; defining a plurality of second contacts, wherein each second contact of the plurality of second contacts comprises a second metal layer over a second substrate; pressing each contact of the plurality of first contacts to a respective second contact of the plurality of second contacts; and heating the plurality of first contacts and the plurality of second contacts to form a metallic alloy between the first metal layer of each contact of the plurality of first contacts pressed to the respective second metal layer of the second contacts of the plurality of second contacts.
 18. The method of claim 17, wherein forming the metallic alloy comprises forming the metallic alloy in direct contact with the first metal layer.
 19. The method of claim 17, wherein the first metal layer comprises Ti, Co, Ni, W, or Pt.
 20. The method of claim 17, wherein the heating is performed at a temperature of about 450° to 500° C. 